Films to make membrane switches (page still under
construction)
Films for membrane switches are available in rolls of 122 (some
in 105) cm width and as panel cut to size.
We devide into these product groups:
Detailed information are available upon request.
Clear Graphic Overlay Films
METOREL GO-CL-VP
Clear Polyester film
with double sided ink-receptive coating. Thicknesses available 0,13 mm, 0,18 mm
and 0,25 mm
The GO-CL VP is a clear polyester film with a
double sided ink- receptive coating for conventional drying screen inks as well
as textured lacTDs suitable for the production of membrane switches and
panels. The good transparency of the film ensures brilliant look of the printed
graphic.
Data:
Haze
< 1%
Light transmission > 90%
Roughness Ra
0,2 - 0,4 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles
> 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,2%
TD / ≤ 1,0 % MD, at 130°C/ 30 min
METOREL CF-T1 PD VP
Heat stabilized
uncoated clear polyester film double sided ink-receptive coating for printing of
conductive inks and insulating inks.
Thicknesses available 0,13 mm, 0,18 mm
and 0,25 mm
Data:
Haze
< 1%
Light transmission > 91%
Roughness Ra
0,2 - 0,5 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,1%
TD / ≤ 0,1 % MD, at 130°C/ 30 min
è to
top
Graphic overlay film matt
METOREL GO-AR-VP
Anti-Reflex film
Polyester film with a
anti reflex coating on the front side, suitable for partial texturing with
UV-curing inks. Ink-receptive coating on reverse side
Thicknesses available:
0,13 mm and 0,18 mm.
The GO-AR VP is a perfect anti-reflex film for the production of membrane
switches as well as sign production. The good transparency of the film as well
as ink-receptive coating will provide excellent printing results.
Front
side coating: Anti-reflex, matt reflexion free suitable for printing of window
printing lacquers
Reverse side:
ink-receptive coating for conventional screen printing inks
Data:
Haze
35 - 45%
Gloss 60° 23 - 29
Roughness Ra
0,9 - 1,3 µm
Embossing possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,7%
TD / ≤ 0,7 % MD, at 130°C/ 30 min
è to
top
METOREL GO-MA-2K VP
Polyester film with a
matt coated front side for printing with 2 component and UV-lacquer, Thicknesses 0,13 mm, 0,18 mm
and 0,25 mm.
The GO-MA-2K-VP is a polyester film with a matt coated front side,
suitable for the production of graphic overlays and signs. The front side
ensures window printing with 2-component and selected UV-window-lacquers to
achieve crystal clear windows. The good transparency of the film as well as ink
receptive coating will provide excellent printing results.
Data:
Haze 65 - 80%
Gloss 60° 13 - 17
Roughness Ra
0,9 - 1,4 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles
> 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,7%
TD / ≤ 0,7 % MD, at 130°C/ 30 min
METOREL GO-MA-UV
Polyester film with a
matt coated front side for window printing with UV- and 2-component lacquers.
Reverse side with ink-receptive coating.
Thicknesses available: 0,13 mm
and 0,18 mm.
The GO-MA-UV is a front side matted polyester film suitable for the production
of graphic overlays and signs. The front side ensures window printing with UV-
and selected 2-component lacquers to achieve crystal clear windows. The good
transparency of the film as well as the ink-receptive coating will provide
excellent printing results.
An additional UV-light
exposure of the front side ensures scratch
resistance of the matt coated surface.
Data:
Haze
50 - 78%
Gloss 60° 13 - 25
Roughness Ra 0,5 - 1,25 µm
Embossing possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,5%
TD / ≤ 1,0 % MD, at 130°C/ 30 min
è to
top
METOREL GO-PU-SM
The GO-PU/SM is a polyurethane film with semi-matt surface
suitable for the production of Membrane Switches. The front side coating allows
windows printing. The high transparency and the ink-receptive coating ensures
best results during the printing process. Additionally the film has excellent
resistance to cold environment as well as an excellent flexibility. The film has
self-healing properties against slight scratches. In outdoor applications the
material is UV-Light resistant. Only a slight change in colour (yellowness) can
occur under UV-radiation.
Base film: Polyurethane film supportive carton, Thickness of
film: 0,20 mm; 0,30 mm; 0,50 mm
Front side: matt, suitable for window printing with UV- and 2 component lacquer
Reverse side coating: By request clear ink-receptive coating for screen printing
inks
Data:
Haze
55 - 65%
Light transmission > 90%
Gloss 60° 12 - 18
Embossing possible
Crack effect
good
Tear strength
excellent
Shore hardness A
85
Folding cycles
> 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,7%
TD / ≤ 0,7% MD, at 80°C/ 30 min
è to
top
Anti-Reflex-Films
METOREL GO-AR-UV
Semi matt overlay film
Polyester film with
semi matt anti-reflex coating, suitable for texturing with UV-lacquers, Reverse
side coating ink-receptive, Thicknesses 0,13 mm and 0,18 mm.
The GO-AR-UV is a Polyester film with an antireflective coating on the front
side, suitable for the production of Membrane Switches or Panels. The good
transparency of the film ensures brilliant look of the printed graphic.
Data:
Haze
19 - 28%
Light transmission 88 - 93%
Gloss 60° 45 - 65
Roughness Ra 0,5 - 1,1 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,5%
TD / ≤ 1,0 % MD, at 130°C/ 30 min
è to
top
Textured Graphic Overlay Films
METOREL GO-DE-FS
Polyester film with
fine textured front side for window printing with UV-lacquers. Reverse side
ink-receptive coating, thicknesses 0,13 mm and 0,18 mm.
the GO-DE/FS received a fine–textured coating on the front side. This film is
suitable to create windows with crystal-clear UV- or 2 component lacquers for
the production of Membrane Switches or Panels. An extra exposure to UV-Light
sources ensures the final scratch and chemical resistance of the surface, when
windows with UV-lacquers are not printed. The reverse side received an
ink-receptive coating for best printing results. The good transparency of the
film ensures brilliant look of the printed graphic
Data:
Haze
75 - 95%
Light transmission 84 - 92%
Gloss 60°
12 - 22
Roughness Ra
1,7 - 2,4 µm
Roughness Rz
10 - 18 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,5%
TD / ≤ 1,0% MD, at 130°C/ 30 min
è to
top
METOREL GO-DE-GS
Polyester film with
heavy textured front side for window printing with UV-lacquers. Reverse side
ink-receptive coating, thicknesses 0,13 mm and 0,18 mm.
the GO-DE/FS received a heavy–textured coating on the front side. This film is
suitable to create windows with crystal-clear UV- or 2 component lacquers for
the production of Membrane Switches or Panels. An extra exposure to UV-Light
sources ensures the final scratch and chemical resistance of the surface, when
windows with UV-lacquers are not printed. The reverse side received an
ink-receptive coating for best printing results. The good transparency of the
film ensures brilliant look of the printed graphic
Data:
Haze
75 - 95%
Light transmission 84 - 92%
Gloss 60° 12 - 22
Roughness Ra 2,4 - 3,4 µm
Roughness Rz 14 - 22 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,5%
TD / ≤ 1,0% MD, at 130°C/ 30 min
è to
top
Circuit Films
METOREL CF-T1
The Polyester film CF-T1 is a heat stabilized uncoated Polyester
film, clear or hazy type available in roll width 105 cm.
Thickness (clear): 0,13 mm, 0,18 mm and 0,25 mm
Thickness (hazy): 0,10 mm, 0,13 mm and 0,19 mm
Data:
Melting point
260°C
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles > 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,1%
TD / ≤ 0,1 % MD, at 130°C/ 30 min
Dielectric strength 180 kV/mm
at 23
µm/25°C/50Hz
Surface resistance 1013 Ohm
Resistivity 1015
Ohm/m at 25°C
è to
top
METOREL CF-T1 PE
The CF-T1/PE is a heat stabilized Polyester film. It has
received a clear ink-receptive coating on one side for conductive pastes and
dielectric ink.
Front side coating: clear ink-receptive, Reverse side coating: none
Thickness (clear): 0,13 mm, 0,18 mm and 0,25 mm
Thickness (hazy): 0,10 mm, 0,13 mm and 0,19 mm
Data:
Melting point
260°C
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles
> 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,1%
TD / ≤ 0,1 % MD, at 130°C/ 30 min
Dielectric strength 180 kV/mm
at 23
µm/25°C/50Hz
Surface resistance 1013 Ohm
Resistivity 1015
Ohm/m at 25°C
METOREL CF-T1 PD VP
Heat stabilized
uncoated clear polyester film double sided ink-receptive coating for printing of
conductive inks and insulating inks.
Thicknesses available 0,13 mm, 0,18 mm
and 0,25 mm
Data:
Haze
< 1%
Light transmission > 91%
Roughness Ra
0,2 - 0,5 µm
Embossing
possible
Crack effect
good
Tear strength
excellent
Folding cycles
> 14.000
Strokes (un-embossed) > 10 Mio
Shrinkage ≤ 0,1%
TD / ≤ 0,1 % MD, at 130°C/ 30 min
è to